Samland PC High-Impact Compound SL-C-PC20H (2000EZ/2100LG Equivalent)

Core Properties: High Optical Clarity with Excellent Impact Strength, Superior Dimensional Stability, Outstanding Heat Resistance

Additional information

Elongation at Break	4–6%
GF Content	20% (±1%)
HDT @1.8 MPa	≥220 °C
MB Density	~1.27 g/cm³
Notched Impact (23 °C)	≥10 kJ/m²
Tensile Modulus	~4,200 MPa
Tensile Strength (dry)	90–110 MPa
Unnotched Charpy Impact	≥50 kJ/m²

Technical Comparison

Property	Pulse™ 2000EZ/2100LG (Trinseo)	SL-C-PC20H (Samland)	Customer Value
Glass Fiber Content	20% (±1%)	20% (±1%)	Comparable reinforcement; seamless material replacement
Elongation at Break	3–4%	4–6%	Higher ductility improves crack resistance and dimensional integrity
HDT @1.8MPa	≥215 °C	≥220 °C	More thermal margin for under-hood and high-temp applications
Density	~1.28 g/cm³	~1.30 g/cm³	Slightly denser, supports robust wall formation
Notched Charpy Impact (23 °C)	≥10 kJ/m²	≥12 kJ/m²	Enhanced toughness for drop or impact-prone components
Tensile Modulus	~4,200 MPa	~4,300 MPa	Slightly stiffer, offers improved shape retention and dimensional control
Tensile Strength (dry)	95–105 MPa	100–115 MPa	Stronger mechanical performance for load-bearing structures
Unnotched Charpy Impact	≥50 kJ/m²	≥55 kJ/m²	Superior vibration resistance and long-term reliability
Melt Flow Rate (MFR)	~18–20 g/10min	~20 g/10min	Smooth flow for precision molding, especially in multi-cavity thin-wall tools
Flame Retardant Grade	UL94 HB / V-2	UL94 V-2 (Standard); V-0 optional	Meets electronic appliance requirements, V-0 available for high safety-critical applications

Samland Unique Advantages:

Reinforced PC-GF20 compound optimized for high strength and heat resistance

Excellent dimensional precision, ideal for complex structures or thin-wall molding

Balanced rigidity and impact resistance, enabling durability in functional parts

Smooth surface finish with good appearance and color uniformity

Stable local supply with MOQ 1 ton and 3–4 week lead time — suitable for trial and scale-up

Competitive pricing vs. imported PC GF20 grades, reducing the total cost of ownership

Application Scenarios:

Automotive structural components — such as instrument panels, trim brackets, functional housings

White goods internal parts — including support frames, connection panels

Consumer electronics — requiring both impact strength and clean appearance

Power tool casings — where mechanical load and dimensional accuracy are key

Office equipment — e.g., printer housings, connectors requiring heat stability

Customer Pain Points Solved

Pain Point	Samland Solution
Brittle failure at low temperatures	≥12 kJ/m² notched impact strength ensures reliable performance in cold or impact-prone environments
Insufficient structural strength in PC-based alloys	~4,300 MPa tensile modulus + 100–115 MPa strength = better support for functional load-bearing parts
Inconsistent mold filling or warpage in complex tools	MFR ~20 g/10min + excellent dimensional precision ensures smooth filling in multi-gate thin-wall molds
Surface aesthetics + impact balance hard to achieve	PC/ABS base with 20% GF offers good surface finish with high impact resistance
Imported PC/ABS GF20 grades cost too much or have long lead times	Localized formula with stable lead time (3–4 weeks) and competitive cost advantage

Application Range

Why Choose Samland

Contact Us / Request a Sample

Phone

+ 86-13726366701

Email

daniel0253007@gmail.com

Address

No.19, Bihua Road, Baishi Village, Sanxiang Town, Zhongshan City, Guangdong Province, China.